| Classification | Unit | 9μm | 12μm | 18μm | 35μm | |
| Cu Content | % | ≥99.8 | ||||
| Area Weigth | g/m2 | 80±3 | 107±3 | 153±5 | 283±7 | |
| Tensile Strength | R.T.(23℃) | Kg/mm2 | ≥28 | |||
| H.T.(180℃) | ≥15 | ≥15 | ≥15 | ≥18 | ||
| Elongation | R.T.(23℃) | % | ≥5.0 | ≥5.0 | ≥6.0 | ≥10 |
| H.T.(180℃) | ≥6.0 | ≥6.0 | ≥8.0 | ≥8.0 | ||
| Roughness | Shiny(Ra) | μm | ≤0.43 | |||
| Matte(Rz) | ≤2.5 | |||||
| Peel Strength | R.T.(23℃) | Kg/cm | ≥0.77 | ≥0.8 | ≥0.8 | ≥0.8 |
| Degraded rate of HCΦ(18%-1hr/25℃) | % | ≤7.0 | ||||
| Change of color(E-1.0hr/200℃) | % | Good | ||||
| Solder Floating 290℃ | Sec. | ≥20 | ||||
| Appearance(Spot and copper powder) | ---- | None | ||||
| Pinhole | EA | Zero | ||||
| Size Tolerance | Width | mm | 0~2mm | |||
| Length | mm | ---- | ||||
| Core | Mm/inch | Inside Diameter 79mm/3 inch | ||||
SEM(Shiny Side after Treatment)
SEM(Rough Side after Treatment)
SEM(Before Surface Treatment)