| Base Material | C11000 Copper, Cu > 99.90% |
| Thickness Range | 0.01mm-0.15mm (0.0004inch~0.006inch) |
| Width Range | 4mm-400mm(0.16inch~16inch) |
| Temper | Hard, Half Hard, Soft |
| Application | Transformer, Copper Flexible Connector, CCL, FCCL, PCB, Geothermal Film, Construction, Decoration etc. |
| Temper | JIS Temper | Tensile Strength Rm/N/mm 2 | Elongation A50/% | Hardness HV |
| M | O | 220~275 | ≥ 15 | 40～60 |
| Y2 | 1/4H | 240~300 | ≥ 9 | 55～85 |
| Y | H | 330~450 | - | 80～150 |
| Density | 8.9g/cm3 |
| Electrical conductivity (20°C) | min 90%IACS for annealed to temper min 80%IACS for rolled to temper |
| Thermal conductivity (20°C) | 390W/(m°C) |
| Elastic modulus | 118000N/m |
| Softening temperature | ≥380°C |
| Thickness | Thickness Tolerances | Width | Width Tolerances |
| 0.01~0.015 | ± 0.002 | 4~250 | ± 0.1 |
| > 0.018~0.10 | ± 0.003 | 4~400 | |
| > 0.10~0.15 | ± 0.005 | 4~400 |
| Thickness | Width | Temper |
| 0.01~0.015 | 4～250 | O,H |
| > 0.018~0.10 | 4～400 | O,H |
| > 0.10~0.15 | 4～400 | O,1/2H,H |
| GB | ALLOY NO. | SIZE (mm) | ||||
| (ISO) | (ASMT) | (JIS) | (BIS) | (DIN) | ||
| T2 | Cu-ETP | C11000 | C1100 | C101 | R-Cu57 | Thickness: 0.01-0.15/Max Width: 400 |
| TU2 | Cu-OF | C10200 | C1020 | Cu-OFC | OF-Cu | |
| Nations | Standard No. | Standard Name |
| China | GB/T2059--2000 | CHINA’S NATIONAL STANDARD |
| Japan | JIS H3100 :2000 | COPPER AND COPPER ALLOY SHEETS,PLATES AND STRIPS |
| U.S.A | ASTM B36/B 36M -01 | STANDARD SPECIFICATION FOR BRASS,PLATE,SHEET,STRIP AND ROLLED BAR |
| Germany | DIN-EN 1652:1997 | COPPER AND COPPER ALLOYS PLATE,SHEET,STRIP AND CIRCLES FOR GENERAL PURPOSES |
| DIN-EN 1758 :1997 | COPPER AND COPPER ALLOYS STRIP FOR LEADFRAMES | |
| SEMI | SEMI G4-0302 | SPECIFICATION FOR INTERGRATED CIRCUIT LEADFRAME MATERIALS USED IN THE PRODUCTION OF STAMPED LEADFRAMES |